# 2.2.1.3 Rubber and Thermoplastic Elastomers

> From: LOCTITE®X Digital Manual for Bonding (https://www.loctitex.com/en/manuals/bonding/2.2.1.3-rubber-and-thermoplastic-elastomers/)

##### 2.2.1.3 Rubber and Thermoplastic Elastomers

_Figure 24 Different parts of rubber_

![Figure 24 Different parts of rubber](/en/manuals/bonding/assets/img/rubber-substrate-bonding.jpg)

Natural Rubber (NR) and thermoplastic elastomers are stable, resilient, easy to work with and highly durable materials. Elastomers are used where their characteristic properties are required, i.e. when rubber-elastic behaviour in the application temperature range is necessary. A distinction can be made between natural rubber (NR) and synthetic rubber, such as styrene-butadiene rubber (SBR), chloroprene rubber (CR), butyl rubber (IIR), ethylene propylene diene rubber (EPDM), butadiene-acrylonitrile rubber (NBR) and silicone rubber (Q). Even though synthetic rubbers have been further developed in recent years, the properties of NR remain unrivalled, especially in terms of permanent elasticity, cold elasticity and abrasion resistance.

According to DIN 7724 and ISO 472, further distinctions are made between elastomers and thermoplastic elastomers.

- Elastomers: rubber elasticity is present at temperatures below 20ºC (70ºF).
- Thermoplastic elastomer: rubber elasticity is present above 20ºC (70ºF) up to the decomposition temperature.